Density |
|
|
Flexural modulus |
|
|
Flexural Strength |
|
|
Impact Strength (unnotched) |
|
|
Elongation at break |
|
|
Tensile Strength |
|
Rupture modulus |
|
Hardness (Barcol) |
|
Hardness (Rockwell) |
|
Heat distortion at 1.82 MN m2 |
|
Linear Thermal Expansion |
|
Thermal Conductivity |
| |
|
|
Flammability |
| |
|
|
Smoke generation |
|
Heat Resistance
(patterned surface) |
|
| Archimedes |
| ISO 178 |
| ISO 178 |
| ISO 179 |
| ASTM D 368 |
| ASTM D 638 |
| ASTM D 760 |
| ASTM D 2583 |
| ISO 2039/2 |
| ASTM D 648 |
| Standard |
| |
| |
| BSD 476:part 7 |
| |
| NeN 3883 |
| |
|
| gcm-3 |
| GN m -2 |
| MN m -2 |
| kj m -2 |
| % |
| MN - 2 |
| MN m -2 |
| Scale |
| Rockwell M |
| .C |
| .C-1 |
| Cal cm/cm2 |
| .C sec |
| Class |
| Class |
| |
| |
|
| 1.7 |
| 12 |
| 130 |
| 5 |
| 2 |
| 70 |
| 80 + - 15 |
| 74 |
| 100 |
| 100 |
| Mean 4.05 x 10 -5 |
| (23.C to 70 .C) |
| 8 x 10 -4 |
| 2 |
| 2 |
| Very low |
| Not marked by |
| pot of oil at 180.C |
| left for 30 minutes |
|